An Exemplar Imidazoline Surfactant for Corrosion Inhibitor Studies: Synthesis,Characterization, and Physicochemical Properties

An optimized one-pot recipe has been developed to synthesize a surfactant molecule, referred to as OMID, consisting of an imidazoline head group and aliphatic tail, which is an exemplar corrosion inhibitor for carbon steel in acidic solutions. As evidenced by gas chromatography, ¹H and ¹³C nuclear magnetic resonance, and Fourier-transform infrared data, a high-purity product was achieved without the use of either a solvent or catalyst. Critical micelle concentration values and corrosion inhibition efficiencies ( η %) were determined in aqueous solutions of hydrochloric acid and sulfuric acid using surface tensiometry and linear polarization resistance measurements, respectively. Hydrolysis of the imidazoline head group as a function of pH (0–11) was explored with ultraviolet–visible absorption spectroscopy. In addition, N 1s and C 1s X-ray photoelectron spectroscopy data were acquired from both surface-adsorbed OMID and a multilayer of the imidazoline head group of OMID. These latter data are highly relevant to those attempting to understand OMID inhibition chemistry.     

铌对取向硅钢冷轧组织织构的影响

采用光学显微镜(OM)、电子背散射衍射(EBSD)等研究了铌对取向硅钢冷轧过程中的组织与织构的影响。结果表明:含铌正火板和不含铌正火板经冷轧后都是条带状组织,但含铌冷轧板在宽度方向更窄。铌元素的存在对织构也具有优化作用,经过中间退火后,含铌冷轧板二次冷轧织构得到明显改善,相较于不含铌二次冷轧板拥有强度较低的旋转立方织构以及强度较高的{111}<112>织构,其取向密度最高可达12.460。     

氮含量对HPD-1双相不锈钢组织及力学性能的影响

通过显微组织观察与力学性能测试研究了氮含量(0.08%~0.22％,质量分数)对HPD-1双相不锈钢硬度、拉伸性能、低温冲击性能及疲劳性能的影响。结果表明,氮含量变化可显著影响试验钢γ/α相比例,当氮含量由0.08％升高到0.22％,γ相含量由38.1％提高至56.5％。α相的硬度由273 HV10提高到343 HV10,γ相的硬度由238 HV10提高到299 HV10,试验钢强度明显提升。氮元素对两相比例和奥氏体相韧性的双重影响导致试验钢低温冲击性能呈先上升后下降的趋势;更高的氮含量抑制疲劳裂纹萌生与拓展,是影响HPD-1双相不锈钢室温疲劳性能的主要因素。撕裂棱是疲劳断口的显著特征。     

Effect of height on the corrosion of steel and galvanized steel in nontropical coastal marine environments

In this study, the behavior of carbon steel and galvanized steel in nontropical coastal marine environments was evaluated. Evaluation was carried out with specimens with dimensions of 10 cm × 10 cm × 0.3 cm. These specimens were exposed to four testing stations (Iquique, Mejillones, Los Vilos, and San Vicente), where racks were installed both at ground level (ground), as well as in the upper zone of electrical transmission towers (tower). In each station, 24 specimens of A36 carbon steel and galvanized steel were placed (12 each). The corrosivity of the environment was measured using the ISO 9223, 9225, and 9226 standards. The specimens were evaluated on-site, monthly, through visual inspection and photographic record. Once withdrawn, the corrosion rate was determined and the corrosion products were analyzed through Raman and Fourier-transform infrared. The results show that, in all cases, the corrosion rate is greater in the tower than on the ground. However, even though the Los Vilos station is located farther from the sea (3,500 vs. ≈500 m), the corrosion rate of steel in the tower is the highest. This is caused by the generation of HCl from the transformation of lepidocrocite into goethite, in the presence of low chloride content, which acidifies the steel/corrosion product interface. In the case of galvanized steel, the corrosion rate is a function of the chloride content in the atmosphere, obtaining an excellent correlation between both parameters.     

Design,Synthesis, and in vitro Evaluation of P2X7 Antagonists

The P2X7 receptor is a promising target for the treatment of various diseases due to its significant role in inflammation and immune cell signaling. This work describes the design, synthesis, and in vitro evaluation of a series of novel derivatives bearing diverse scaffolds as potent P2X7 antagonists. Our approach was based on structural modifications of reported (adamantan-1-yl)methylbenzamides able to inhibit the receptor activation. The adamantane moieties and the amide bond were replaced, and the replacements were evaluated by a ligand-based pharmacophore model. The antagonistic potency of the synthesized analogues was assessed by two-electrode voltage clamp experiments, using Xenopus laevis oocytes that express the human P2X7 receptor. SAR studies suggested that the replacement of the adamantane ring by an aryl-cyclohexyl moiety afforded the most potent antagonists against the activation of the P2X7 cation channel, with analogue 2-chloro-N-[1-(3-(nitrooxymethyl)phenyl)cyclohexyl)methyl]benzamide ( 56 ) exhibiting the best potency with an IC₅₀ value of 0.39 μM.     

汉语谐音与语义双关语的认知神经加工差异——ERP证据

该文运用事件相关电位技术,观测汉语谐音双关语与语义双关语两者是否存在认知神经加工上的差异。结果发现,语义双关语的正确率明显低于谐音双关语以及不符合逻辑语篇的正确率。谐音双关语组、语义双关语组和不合逻辑语篇引发的脑电波数据在300～900ms之间存在显著差异。其中,语义双关语和不合逻辑语篇都引发了N400效应。脑电波形图和脑电波地形图显示,前者引发的N400效应略微晚于后者引发的N400效应,但数据统计的结果不显著。在600～900ms,谐音双关语引发了P600效应。研究由此推论: 汉语谐音双关语与语义双关语认知层面的加工差异与双关语的呈现形式和表达效果密切相关。     

ASME Ⅱ卷D篇表U数据作为设计校核中材料验收标准存在问题及探讨

ASME标准钢板对于短时高温抗拉数据无规定,但设备设计人员在校核时又要用到此数据,于是有些设计文件在技术要求中将ASME II卷表U的数据作为材料验收的标准。针对此种做法引发的争议及涉及的主要问题进行试验验证和分析探讨。研究结果表明,ASME II卷D篇表U中的数据是基于室温抗拉强度保证值,并根据拟合曲线将室温保证值提高了10%得到的,实测数据与ASME规范数据不一致,部分材料在250~350℃存在动态应变时效现象,但仍不满足设计要求。材料经模拟焊后热处理后性能下降,难以到达交货态的要求。给出了短时高温抗拉强度的选用建议。     

低活化马氏体钢热变形行为及机理型本构建模研究

利用Gleeble-3500热模拟试验机研究了低活化马氏体钢在变形温度为850～950 ℃、应变速率为0.001～1 s^-1条件下的热变形行为。建立了流变应力本构方程，并评估了该方程的预测能力。绘制了低活化马氏体钢在不同应变下的热加工图。结果表明：在较高的应变速率条件下，该材料主要发生动态回复，在较高变形温度和较低应变速率下具有明显的动态再结晶特征；本构方程的预测结果与实验结果符合良好；变形温度870～930 ℃、应变速率0.001～0.01 s^-1和变形温度920～950 ℃、应变速率0.3～1 s^-1分别是真应变为0.4和0.6下最优的热加工区域。     

浅析火力发电厂汽水系统中内径管与外径管的设计选择

按照管道加工工艺的不同,管道可分为内径控制管和外径控制管。通过热轧工艺生产的外径控制无缝钢管,可满足火力发电厂汽水系统中绝大部分管道的使用要求。对于超(超)临界机组的主蒸汽和高温再热蒸汽管道采用的P91/P92材质的大口径厚壁无缝钢管,由于对材料性能和加工工艺有特殊要求,因此宜采用内径控制管。     

中国钢化联产发展现状与前景展望

中国是一个钢铁生产大国,也是一个油气资源相对不足、煤炭资源相对丰富的国家。基于中国能源结构的实际情况,结合钢铁行业和化工行业的发展现状,讨论了钢铁生产各个工序煤气的发生与使用情况,并对钢铁流程副产煤气合成化工产品的现状与潜力进行了分析,指出了存在的问题。结合分析结果,提出了未来可再生能源廉价制氢发展达到一定阶段,钢铁联合企业可以通过“以氢固碳”实现钢铁生产大规模减少CO₂排放的目标,提升其清洁能源转化与高附加值化工产品生产的社会功能。最后,对未来中国钢化联产的发展提出了建议。